Colors
FGF PIPG Glassfiber (19%) is available in 5 colors.
Standard
FGF PIPG Glassfiber (19%)
PIPG filled with glassfiber to improve the impact strength in combination with an economical solution.
Exists for 81% out of post-industrial PET-G.
Features
- High impact
- Stiff
- 19% glassfiber
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,37 g/cc |
| MFR 200°C/5 kg | ISO 1133 | 1,2 g/10 min |
| Tensile strength at yield | ISO 527 | 76 MPa |
| Tensile strength at break | ISO 527 | 76 Mpa |
| Elongation-Strain at yield | ISO 527 | 2,7% |
| Elongation-Strain at break | ISO 527 | 3,2% |
| Tensile modulus | ISO 527 | 1900 MPa |
| Impact strength - Charpy notched 23˚C | ISO 179 | 7,5 kJ/m² |
| Vicat softening temperature | ISO 306 | N/A |
| Mold shrinkage | internal method (ISO 294-4 based ) | 0,14% |
| Thermal expansion coëfficient | ISO 11359 | 9,4*10^-5 mm/mm°C |
| Description | Typical value |
|---|---|
| Drying | 4hr,65°C. <400ppm |
| Zone 1 Temperature | 230±20 °C |
| Zone 2 Temperature | 230±20 °C |
| Zone 3 Temperature | 230±20 °C |
| Mass temperature | 230-250 °C |
| Die temperature | 230±20 °C |
Packaging
FGF PIPG Glassfiber is available in 20kg bag
Additional information
The glassfiber is mildly abrasive, please consider the use of a hardened steel nozzle and, if used, a gear pump,
when printing with FGF PIPG Glassfiber.Do not use a breaker plate with screen.
Storage
Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.