FGF recycled PP Glassfiber (30%) is available in the color black



FGF Recycled PP Glassfiber (30%)

FGF Recycled ASA-X 20% Glassfiber is our own specially developed modified ASA compound, made from our own industrial waste, this FGF Recycled PP Glassfiber (30%) is our FGF printable stiff Polypropylene. This has been developed specially for large scale printing by reducing the warping, while maintaining mechanical performance and a good layer adhesion. PP FGF stiffness and chemical/fatigue resistance makes it suitable for a variety of larger scale applications. This grade is made with post industrial recovered PP.


  • High strength
  • Good chemical resistance
  • Easy to print
  • Almost no warping
  • 30% glassfiber

Description Test method Typical value
Specific gravity ISO 1183 1,13 g/cc
MFR 200°C/5 kg ISO 1133 10 g/10min
Tensile strength at yield ISO 527 75 MPa
Tensile strength at break ISO 527 75 MPa
Elongation-strain at yield ISO 527 2,6%
Elongation-strain at break ISO 527 3,4%
Tensile modulus ISO 527 6400 Mpa
Impact strength - Charpy notched 23˚C ISO 179 5,8 kJ/m2
Impact strength – Izod method notched 23°C ISO 180 8 kJ/m2
Flexural modulus ISO 178 4600 Mpa
Flexural strength ISO 178 95 MPa
Vicat softening temperature B50 ISO 306 110°C
Description Typical value
Drying 4hr,70°C. <1000ppm
Zone 1 Temperature 230±20 °C
Zone 2 Temperature 230±20 °C
Zone 3 Temperature 230±20 °C
Mass temperature 230°C
Die temperature 230±20 °C


FGF Recycled PP Glassfiber (30%) is available in 20kg bag

Additional information

The glassfibre is mildly abrasive, please consider the use of a hardened steel nozzle when printing with FGF
Recycled PP Glassfiber (30%). Do not use a breaker plate with screen.


Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.
Get in touch