FGF Recycled PLA MATT
FGF Recycled PLA MATT is an easy to print variant on the everyday material PLA, with an aesthetical matt effect. Its surface diffuses light to give it a matt look and creates a rough feeling. PLA MATT is slightly abrasive, please consider using a hardened nozzle.
Features
- Matt effect, low light refraction
- Easy to print rough surface
- Reliable bed adhesion
- Improved printing speed compared to PLA
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,38 g/cc |
| MFR 200°C/5 kg | ISO 1133 | 32,3 g/10min |
| Tensile strength at yield | ISO 527 | 47 MPa |
| Tensile strength at break | ISO 527 | 50 MPa |
| Elongation-strain at yield | ISO 527 | 2,2% |
| Elongation-strain at break | ISO 527 | 1,8% |
| Tensile modulus | ISO 527 | 5750 Mpa |
| Impact strength - Charpy notched 23˚C | ISO 179 | 1,9 kJ/m2 |
| Vicat softening temperature | ISO 306 | 58°C |
| Mold shrinkage | internal method (ISO 294-4 based ) | 0,09% |
| Description | Typical value |
|---|---|
| Drying | 6hr,50°C*. <250ppm |
| Zone 1 Temperature | 180±20 °C |
| Zone 2 Temperature | 190±20 °C |
| Zone 3 Temperature | 200±20 °C |
| Mass temperature | 209°C |
| Die temperature | 210±20 °C |
Packaging
FGF recycled PLA MATT is available in 20kg bag
Additional information
*As PLA materials crystallize, it is advised to either have an agitated dryer, or dry at a lower temperature for a longer period. This avoids that the pellets stick to each other during drying. Please consider the use of a hardened steel nozzle and, if used, a gear pump, when printing with PLA MATT. The matting agent is mildly abrasive and will result in faster wear of brass nozzles
Storage
Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.