Colors
Available in a homogenous color (dark grey/blue)
FGF Recycled ASA-X 20% Glassfiber
FGF Recycled ASA-X 20% Glassfiber is our own specially developed modified ASA compound, made from our own industrial waste, this ensures the quality of the product. The low warpage ASA compound with added glassfibers gives great features which work well with a variety of applications.
Features
- 20% filled with Glassfiber
- Low warpage
- Easy to print
- UV resistant
- Good layer adhesion
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,27 g/cc |
| MFR 200°C/5 kg | ISO 1133 | 16 g/10min |
| Tensile strength at yield | ISO 527 | 81 MPa |
| Tensile strength at break | ISO 527 | 81 MPa |
| Elongation-strain at yield | ISO 527 | 2,2% |
| Elongation-strain at break | ISO 527 | 2,4% |
| Tensile modulus | ISO 527 | 6300 Mpa |
| Impact strength - Charpy notched 23˚C | ISO 179 1eA | 6,2 kJ/m2 |
| Vicat softening temperature | ISO 306 B50 | 85°C |
| Shrinkage (linear mold) | Internal method | 0,3% |
| Mold shrinkage | internal method (ISO 294-4 based ) | 0,54% |
| Description | Typical value |
|---|---|
| Drying | 4hr,75°C. <250ppm |
| Zone 1 Temperature | 220±20 °C |
| Zone 2 Temperature | 220±20 °C |
| Zone 3 Temperature | 220±20 °C |
| Mass temperature | 220°C |
| Die temperature | 230±20 °C |
Packaging
FGF Recycled ASA-X 20% Glassfiber is available in 20kg bag
Additional information
The glassfibre is mildly abrasive, please consider the use of a hardened steel nozzle when printing with FGF Recycled ASA-X 20% Glassfiber. Do not use a breaker plate with screen.
Storage
Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.