FGF PLA Stone
FGF PLA Stone contains ~50% stone powder. The material is heavier than normal PLA and shows a nice matte finish. FGF PLA Stone shows excellent print results. It gives the feeling of real stone, because of the higher weight of the material.
- Matt surface finish
- Stone look
- Heavier than normal PLA
- Based on PLA
|Description||Test method||Typical value|
|Specific gravity||ISO 1183||1,7 g/cc|
|MFR 210°C/2,16 kg||ISO 1133||5,6 g/10min|
|Tensile strength at yield||ISO 527||44 MPa|
|Tensile strength at break||ISO 527||44 Mpa|
|Elongation-strain at yield||ISO 527||1,7%|
|Elongation-strain at break||ISO 527||1,8%|
|Tensile modulus||ISO 527||6365 MPa|
|Impact strength - Charpy notched 23˚C||ISO 179||3,1 kJ/m2|
|Vicat softening temperature||ISO 306||57,7˚C|
|Mold shrinkage||internal method (ISO 294-4 based )||N/A|
|Zone 1 Temperature||160±20 °C|
|Zone 2 Temperature||175±20 °C|
|Zone 3 Temperature||185±20 °C|
|Die temperature||195±20 °C|
PackagingFGF PLA Stone is available in 20kg bag
*As PLA materials crystallize, it is advised to either have an agitated dryer, or dry at a lower temperature for a
longer period. This avoids that the pellets stick to each other during drying.
The stone is mildly abrasive. Please consider the use of a hardened steel nozzle and, if used, a gear pump, when
printing with FGF PLA Stone. The stone powder is mildly abrasive and can result in faster wear of brass nozzles.