FGF recycled PP Glassfiber (30%) is available in the color black
Standard
FGF Recycled PP Glassfiber (30%)
FGF Recycled ASA-X 20% Glassfiber is our own specially developed modified ASA compound, made from our own industrial waste, this FGF Recycled PP Glassfiber (30%) is our FGF printable stiff Polypropylene. This has been developed specially for large scale printing by reducing the warping, while maintaining mechanical performance and a good layer adhesion. PP FGF stiffness and chemical/fatigue resistance makes it suitable for a variety of larger scale applications. This grade is made with post industrial recovered PP.
Features
- High strength
- Good chemical resistance
- Easy to print
- Almost no warping
- 30% glassfiber
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,13 g/cc |
| MFR 200°C/5 kg | ISO 1133 | 10 g/10min |
| Tensile strength at yield | ISO 527 | 75 MPa |
| Tensile strength at break | ISO 527 | 75 MPa |
| Elongation-strain at yield | ISO 527 | 2,6% |
| Elongation-strain at break | ISO 527 | 3,4% |
| Tensile modulus | ISO 527 | 6400 Mpa |
| Impact strength - Charpy notched 23˚C | ISO 179 | 5,8 kJ/m2 |
| Impact strength – Izod method notched 23°C | ISO 180 | 8 kJ/m2 |
| Flexural modulus | ISO 178 | 4600 Mpa |
| Flexural strength | ISO 178 | 95 MPa |
| Vicat softening temperature B50 | ISO 306 | 110°C |
| Description | Typical value |
|---|---|
| Drying | 4hr,70°C. <1000ppm |
| Zone 1 Temperature | 230±20 °C |
| Zone 2 Temperature | 230±20 °C |
| Zone 3 Temperature | 230±20 °C |
| Mass temperature | 230°C |
| Die temperature | 230±20 °C |
Packaging
Additional information
The glassfibre is mildly abrasive, please consider the use of a hardened steel nozzle when printing with FGF
Recycled PP Glassfiber (30%). Do not use a breaker plate with screen.