Colors
PEI ULTEM™ 9085 is available in 1 color.
Standard
NA1 233 Naturel
PEI ULTEM™ 9085
PEI ULTEM™ 9085 (Polyether Imide) is a high-performance polymer with excellent mechanical performance. This material is UL 94-V0 rated and has a glass transition temperature (Tg) of 186 °C. PEI ULTEM™ 9085 is perfect for applications in for example the aerospace-, automotive- and electrical industry. This material is a combination of exceptional dimensional stability, excellent thermal properties and good chemical resistance.
Features
- Low smoke evolution
- High thermal properties
- Excellent chemical resistance
- Flame retardant
- High glass transition temperature (Tg)
| Size | ø Tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,34 g/cc |
| MFI 340ºC/5kg | ISO 1133 | 30 g/10 min |
| Tensile strength at yield | ISO 527 | 88 MPa |
| Tensile strength at break | ISO 527 | 71 MPa |
| Elongation strain at break | ISO 527 | 50% |
| Elongation strain at yield | ISO 527 | 6,7% |
| Tensile (E) modulus | ISO 527 | 3050 MPa |
| Impact strength - Charpy method 23˚C | ISO 179 | 11 kJ/m² |
| Flammability behaviour | UL94 | V-0 |
| Flexural modulus | ISO 178 | 2750 MPa |
| Flexural strength | ISO 178 | 90 MPa |
| Vicat softening temp. B120 | ISO 306 | 173°C |
| Heat deflection temp. A | ISO 75 | 152°C |
| Description | Test method | Typical value |
|---|---|---|
| printing temp. | Internal method | 380±15˚C |
Packaging
PEI ULTEM™ 9085 is available on polycarbonate and carton spools.Ask our team to help you customizing your product.
Additional information
Recommended temperature for heated bed is ≥120°C. Adhesion is possible on different surfaces. PEI ULTEM™ 9085 can be used on desktop FDM or FFF technology 3D printers able to reach the high required temperatures. Dry the spool before printing: +4 hours at max. 110°C.