3DIAKON™ @MITSUBISHI CHEMICAL

3DIAKON™ PMMA or Poly(methyl methacrylate) is a transparent thermoplastic. It is known as having excellent weathering and UV stability combined with excellent impact performance and stiffness. PMMA is characterized as a transparent material (more transparent after post processing) and it is reasonable easy to print.

Features

  • Strong, lightweight and rigid material
  • High impact resistant
  • Good abrasion resistance
  • Transparent and glossy after post processing (sanding)
  • UV resistance
  • BPA free
Size ø Tolerance Roundness
1,75mm ø 0,05mm 95%
2,85mm ø 0,10mm 95%
Description Test method Typical value
Specific gravity ISO 1183 1,14 g/cc
MFI 230°C/3,8 kg ISO 1133 1,7 g/10 min
Tensile strength at yield ISO 527 43 MPa
Impact Strength Charpy method 23°C (notched) ISO 179 6,2 kJ/m²
Flexural modulus ISO 178 1900 MPa
Flexural Strength ISO 178 62 MPa
Vicat softening temperature ISO 306B 91°C
Heat deflection temperature HDT B ISO 75A 93°C
Transmittance ASTM D1003 91.5°C
Description Test method Typical value
printing temp. Internal method 255±10˚C

Packaging

3Diakon™ is available in the original packaging of Mitsubishi Chemical.

Additional information

We recommend to print large objects of 3Diakon™ in heated chambers to create a nice and smooth printed object. Storage: Cool and dry (15-25°C), this enhances the shelf life signifi cantly.

Storage

In order to prevent moisture pick up and contamination, supplied packaging should be kept closed and undamaged. For the same reason, partially used bags should be sealed before re-storage. Allow the material that has been stored elsewhere to adapt to the temperature in the processing room while keeping the bag closed.