Colors
LUVOCOM® 3F PEEK CF 9676 BK is available in 1 color.
Standard
NA1 230 Black
LUVOCOM® 3F PEEK CF 9676 BK
LUVOCOM® 3F PEEK CF 9676 BK has outstanding mechanical properties in combination with its excellent thermal and chemical resistance. LUVOCOM® 3F PEEK CF 9676 BK is a material from LEHVOSS. It is a flame retardant polyetheretherketone reinforced with carbon fibers The carbon fiber improves the stiffness and compressive strength enormously This material is suitable for dynamically stressed parts, aerospace applications and applications which require inherent flame resistance.
Features
- Outstanding temperature and chemical resistance
- Very high strength and stiffness
- Suitable for dynamically-stressed parts
- Flame retardant
- Low smoke and toxic gas emissions
| Size | ø Tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,36 g/cc |
| MFI 380°C/10kg | ISO 1133 | 16 g/10 min |
| Tensile strength at yield | ISO 527 | 126 MPa |
| Elongation strain at yield | ISO 527 | 3,9% |
| Tensile (E) modulus | ISO 527 | 7800 MPa |
| Impact strength - Charpy notched 23˚C | ISO 179 1eA | 7 kJ/m² |
| Flammability behaviour | UL94 | V-0 |
| Heat deflection temp. A (1,8MPa) | ISO 75 | 280°C |
| Mold shrinkage | DIN 16742 | 0,2-0,4% |
| Description | Test method | Typical value |
|---|---|---|
| printing temp. | Internal method | 425±25˚C |
Packaging
LUVOCOM® 3F PEEK CF 9676 BK is available on polycarbonate and carton spools.Ask our team to help you customizing your product.
Additional information
Recommended temperature for heated bed is ≥110°C. Adhesion is possible on different surfaces. LUVOCOM® 3F PEEK CF 9676 BK can be used on desktop FDM or FFF technology 3D printers able to reach the required temperatures. Dry the spool before printing: 6-8 hours at max. 120°C or 4 hours at 130°C.
*Please consider the use of a hardened steel nozzle when printing with LUVOCOM® 3F PEEK CF 9676 BK. The carbon fibers are abrasive and will result in fast wear of regular brass nozzles. Note: brass nozzles are not allowed this contains copper which is reactive with PEEK.