LUVOCOM® 3F PP CF 9928 BK is available in the color black.

Standard

NA1 238 Black

LUVOCOM® 3F PP CF 9928 BK

LUVOCOM® 3F PP CF 9928 BK is polypropylene copolymer reinforced with carbon fiber. LUVOCOM® 3F PP CF 9928 BK is a material from LEHVOSS. It is suitable for continuous discharging of statically-generated electricity. Recommended for strong and stiff parts.

Features:

  • Strong and stiff parts
  • Inherent good chemical resistance
  • ESD surface resistance 107Ω
  • Low warpage
Size ø Tolerance Roundness
1,75mm ø 0,05mm 95%
2,85mm ø 0,10mm 95%
Description Test method Typical value
Specific gravity ISO 1183 1 g/cc
Tensile strength at yield ISO 527 54 MPa
Elongation strain at yield ISO 527 1,2%
Tensile (E) modulus ISO 527 3400 MPa
Flexural strength ISO 178 78 MPa
Flexural modulus ISO 178 6000 MPa
Vicat softening temp. A ISO 306 80°C
Mold shrinkage DIN 16742 0,2-0,6%
Water absorption 23°C ISO 62 <0,3%
Surface resistance IEC 60093 ≤10^7 Ω
Description Test method Typical value
printing temp. Internal method 225±5˚C

Packaging

LUVOCOM® 3F PP CF 9928 BK is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional information

Recommended temperature for heated bed is ± 65-75˚C. Adhesion is possible on different surfaces. Please consider special PP adhesives for 3D-printing. LUVOCOM® 3F PP CF 9928 BK can be used on all common desktop FDM technology or FFF 3D printers. Level of electrical dissipative properties depends on printing conditions. Dry the spool before printing: 4-6 hours at max. 80°C.
*Please consider the use of a hardened steel nozzle when printing with LUVOCOM® 3F PP CF 9928 BK. The carbon fibers are abrasive and will result in fast wear of regular brass nozzles.

Storage

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.