Colors

LUVOCOM® 3F PEKK 50082 50082 NT is available in natural color.

Standard

NA1 231 Naturel

LUVOCOM® 3F PEKK 50082 NT

LUVOCOM® 3F PEKK 50082 NT (Polyether Ketone Ketone) is a semi-crystalline thermoplastic in the polyaryletherketone family. LUVOCOM® 3F PEKK 50082 NT is a material from LEHVOSS. This material has a very good layer adhesion and dimensional stability. LUVOCOM® 3F PEKK 50082 NT is unique compared to the standard PEKK materials because it prints semi crystalline and it provides improved printability and layer adhesion. This neat PEKK enables semi-crystalline parts with no warping.

Features

  • Outstanding temperature and chemical resistance
  • Excellent mechanical properties
  • Flame retardant
  • Unique tribological properties
Size ø Tolerance Roundness
1,75mm ø 0,05mm 95%
2,85mm ø 0,10mm 95%
Description Test method Typical value
Specific gravity ISO 1183 1,27 g/cc
MFI 380°C/2,16kg ISO 1183 25 g/10 min
Tensile strength at yield ISO 527 90 MPa
Elongation strain at yield ISO 527 5%
Tensile (E) modulus ISO 527 3000 MPa
Flexural modulus ISO 178 2500 MPa
Flexural strength ISO 178 150 MPa
Heat deflection temp. A (1,8MPa) ISO 75 (printed) 160°C
Flammability behaviour UL94 V-0
Mold shrinkage DIN 16742 0,2-0,4%
Description Test method Typical value
printing temp. Internal method 360±20˚C

Packaging

LUVOCOM® 3F PEKK 50082 NT is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional information

Recommended temperature for heated bed is ≥110°C. Adhesion is possible on different surfaces. LUVOCOM® 3F PEKK 50082 NT can be used on desktop FDM or FFF technology 3D printers able to reach the required temperatures. Dry the spool before printing: 6-8 hours at max. 120°C or 4 hours at 130°C.

Storage

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.