Colors
LUVOCOM® 3F PEEK 9581 NT is available in natural color.
Standard
NA1 229 Naturel
LUVOCOM® 3F PEEK 9581 NT
LUVOCOM® 3F PEEK 9581 NT is based on polyetheretherketone (PEEK), one of the highest performing engineering thermoplastics in the world and can replace metals and composites. LUVOCOM® 3F PEEK 9581 NT is a material from LEHVOSS. LUVOCOM® 3F PEEK 9581 NT is an unreinforced grade and can be used for multiple applications in different industries; aerospace-, gas-, oil-, automotive- and the medical industry. This semi crystalline thermoplastic provides high temperatures, excellent mechanical and chemical resistance properties. The excellent layer adhesion of LUVOCOM® 3F PEEK 9581 NT improves the impact resistance, strength, durability and the printing process.
Features
- Outstanding temperature and chemical resistance
- High strength, including z-layers
- Flame retardant
- Cytotoxicity proliferation according EN ISO 10993-1
| Size | ø Tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,31 g/cc |
| MFI 380°C/10kg | ISO 1133 | 29 g/10 min |
| Tensile strength at yield | ISO 527 | 97 MPa |
| Elongation strain at yield | ISO 527 | 5% |
| Tensile (E) modulus | ISO 527 | 3800 MPa |
| Flexural strength | ISO 178 | 145 MPa |
| Flexural modulus | ISO 178 | 3400 MPa |
| Impact strength - Charpy notched 23˚C | ISO 179 1eA | 7 kJ/m² |
| Flammability behaviour | UL94 | V-0 |
| Heat deflection temp. A (1,8MPa) | ISO 75 | 145°C |
| Description | Test method | Typical value |
|---|---|---|
| printing temp. | Internal method | 395±25˚C |
Packaging
LUVOCOM® 3F PEEK 9581 NT is available on polycarbonate and carton spools.Ask our team to help you customizing your product.
Additional information
Recommended temperature for heated bed is ≥110°C. Adhesion is possible on different surfaces. LUVOCOM® 3F PEEK 9581 NT can be used on desktop FDM or FFF technology 3D printers able to reach the required temperatures. Dry the spool before printing: 6-8 hours at max. 120°C or 4 hours at 130°C.
Note: brass nozzles are not allowed – this contains copper which is reactive with PEEK.