Colors

LUVOCOM® 3F PAHT CF 9891 BK is available in the color black.

Standard

NA1 237 Black

LUVOCOM® 3F PAHT CF 9891 BK

LUVOCOM® 3F PAHT CF 9891 BK is a 15% carbon fiber reinforced material. LUVOCOM® 3F PAHT CF 9891 BK is a material from LEHVOSS. It is designed for industrial applications, easy to print with low warping an increased layer adhesion. LUVOCOM® 3F PAHT CF 9891 BK is a PA6 based material, it has a low influence from moisture and temperature on dimensional stability and electrical properties.

Features:

  • Carbon Fiber Reinforced Material (15%)
  • Extremely stiff
  • Designed for industrial applications
  • PA6 based material
  • Low warping and increased layer adhesion
Size ø Tolerance Roundness
1,75mm ø 0,05mm 95%
2,85mm ø 0,10mm 95%
Description Test method Typical value
Specific gravity ISO 1183 1,24 g/cc
MFI 250ºC/2,16kg ISO 1133 4 g/10 min
Tensile strength at yield ISO 527 120 MPa
Elongation strain at yield ISO 527 2%
Tensile (E) modulus ISO 527 10500 MPa
Impact Strength - Charpy method 23°C Unnotched ISO 179 1eA U 35 kJ/m2
Mold shrinkage DIN 16742 0,3-0,5%
Water absorption 23°C ISO 62 <0,3%
Description Test method Typical value
printing temp. Internal method 260±5˚C

Packaging

LUVOCOM® 3F PAHT CF 9891 BK is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional information

Recommended temperature for heated bed is 65-75˚C. Adhesion is possible on different surfaces. LUVOCOM® 3F PAHT CF 9891 BK can be used on all common desktop FDM technology or FFF 3D printers. Dry the spool before printing: 12 hours at 70°C or 4 hours at 100°C. *Please consider the use of a hardened steel nozzle when printing with LUVOCOM® 3F PAHT CF 9891 BK. The carbon fibers are abrasive and will result in fast wear of regular brass nozzles.

Storage

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.