LUVOCOM® 3F PAHT 9936 BK

LUVOCOM® 3F PAHT 9936 BK is an unreinforced polyamide-based formulation. LUVOCOM® 3F PAHT 9936 BK is a material from LEHVOSS. LUVOCOM® 3F PAHT 9936 BK has excellent tensile and impact strength and allows continued operation up to 100°C – 120°C while retaining 50% of its mechanical properties and short-term 160°C.

Features:

  • Unreinforced PAHT
  • Optimized surface appearance
  • Designed for industrial applications
  • PA6 based material
  • Low warping and increased layer adhesion
Size ø Tolerance Roundness
1,75mm ø 0,05mm 95%
2,85mm ø 0,10mm 95%
Description Test method Typical value
Specific gravity ISO 1183 1,25 g/cc
MFI 250ºC/2,16kg ISO 1133 6 g/10 min
Tensile strength at yield ISO 527 78 MPa
Elongation strain at yield ISO 527 4,4%
Tensile (E) modulus ISO 527 3400 MPa
Flexural modulus ISO 178 6000 MPa
Flexural strength ISO 178 78 MPa
Vicat softening temp. A ISO 306 80°C
Heat deflection temp. A (1,8MPa) ISO 75 90°C
Mold shrinkage DIN 16742 0,3-0,5%
Water absorption 23°C ISO 62 <0,3%
Description Test method Typical value
printing temp. Internal method 265±10˚C

Packaging

LUVOCOM® 3F PAHT 9936 BK is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional information

Recommended temperature for heated bed is ± 60-70˚C. Adhesion is possible on different surfaces. LUVOCOM® 3F PAHT 9936 BK can be used on all common desktop FDM technology or FFF 3D printers. Dry the spool before printing: 12 hours at 70°C or 4 hours at 100°C.

Storage

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.