Colors

LUVOCOM® 3F PAHT 9825 NT is available in its natural colour.

Standard

NA1 235 Naturel

LUVOCOM® 3F PAHT 9825 NT

LUVOCOM® 3F filament PAHT 9825 NT is a high temperature resistant polyamide (PA) -based, unfilled material. It has the strength of a PA6 without affecting its printability. LUVOCOM® 3F PAHT 9825 NT is a material from LEHVOSS. 3D-printed components made from this material have high strength and toughness. It has a low influence from moisture and temperature on dimensional stability and electrical properties. Can be used in the automotive industry, textile- and office machinery, apparatus- and precision engineering.

Features:

  • Unreinforced PAHT
  • Designed for industrial applications
  • PA6 based material
  • Low warping and increased layer adhesion
  • Strong and tough parts
Size ø Tolerance Roundness
1,75mm ø 0,05mm 95%
2,85mm ø 0,10mm 95%
Description Test method Typical value
Specific gravity ISO 1183 1,2 g/cc
MFI 250ºC/2,16kg ISO 1133 4 g/10 min
Tensile strength at yield ISO 527 85 MPa
Elongation strain at yield ISO 527 3,6%
Tensile (E) modulus ISO 527 3400 MPa
Heat deflection temp. A (1,8MPa) ISO 75 90°C
Mold shrinkage DIN 16742 0,3-0,5%
Water absorption 23°C ISO 62 <0,3%
Description Test method Typical value
printing temp. Internal method 265±10˚C

Packaging

LUVOCOM® 3F PAHT 9825 NT is available on polycarbonate and carton spools.
Ask our team to help you customizing your product.

Additional information

Recommended temperature for heated bed is ± 60-70˚C. Adhesion is possible on different surfaces. LUVOCOM® 3F PAHT 9825 NT can be used on all common desktop FDM technology or FFF 3D printers. Dry the spool before printing: 12 hours at 70°C or 4 hours at 100°C.

Storage

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.