Novamid® ID1070 is available from stock in:


BK1 Black
WH1 White


NOVAMID® ID1070 is a strong and ductile 3D printing grade based on PA6. It is a high-quality polyamide, that has been developed as a special product line in order to cope with high demand levels from our Japanese customers. Novamid® ID1070 has seen various applications in various fields and various regions. From car to packaging, Novamid® is supported by an experienced and wide range of experts.


  • Is a pure polyamide 6, and was originally developed many years ago by our Engineering Plastics experts for demanding specialty applications often subjected to extreme heat.
  • The optimized crystallization profile improves fusion, enabling parts with excellent interlayer strength and high surface quality.
Size ø Tolerance Roundness
1,75mm ø 0,05mm 95%
2,85mm ø 0,10mm 95%
Description Test method Typical value
Tensile modulus ISO 527-1/-2 2590 / 710 MPa
Yield stress ISO 527-1/-2 77 / 40 MPa
Stress at break ISO 527-1/-2 46.5 / 47.5 MPa
Strain at break ISO 527-1/-2 >50 / >50 %
Charpy impact strength (+23°C) ISO 179/1eU N / - kJ/m²
Description Test method Typical value
printing temp. Internal method 260±10˚C


Novamid® ID1070@DSM is available in the original packaging of DSM.

Additional information

Common fused filament fabrication (FFF) equipment should work with Novamid® filaments, direct drive as well as Bowden type extruders. Typical settings for any slicing software (e.g. Slic3R, Cura, Simplify3D) are listed below. Note that for different nozzle diameters the settings should be changed accordingly.


In order to prevent moisture pick up and contamination, supplied packaging should be kept closed and undamaged. For the same reason, partially used bags should be sealed before re-storage. Allow the material that has been stored elsewhere to adapt to the temperature in the processing room while keeping the bag closed.