Colors
PLA SATIN is available from stock in the following colors.
For non stock colors a minimum of 40kg ± 10% is required.
Satin
BUS Blue Satin
GOS Gold Satin
GRS Gren Satin
PIS Pink Satin
PUS Purple Satin
RAS Raspberry Satin
SIS Silver Satin
WHS White Satin
YFS Yellow Fluor Satin
PLA Satin
PLA Satin is a PLA based material developed for its silky and smooth shine. It increases the perception of color brilliance and disperses light when viewed from different angles giving a unique glossy effect. Slower printing and low temperature improve the silky effect. The satin surface creates beautiful reflection in printed objects.
PLA Satin features:
- High light reflection
- Smooth and silky
- Fantastic Satin look
- Deep colors
| Size | ø Tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,24 g/cc |
| MFR 210°C/2,16 kg | ISO 1183 | 8,2 g/10 min |
| Tensile strength at yield | ISO 527 | 71 MPa |
| Tensile strength at break | ISO 527 | 71 MPa |
| Elongation strain at yield | ISO 527 | 3,2% |
| Elongation strain at break | ISO 527 | 3,6% |
| Tensile (E) modulus | ISO 527 | 3200 MPa |
| Impact strength - Charpy method 23˚C | ISO 179 1eA | 2,6 kJ/m2 |
| Vicat softening temp. | ISO 306 B50 | 58,2°C |
| Description | Test method | Typical value |
|---|---|---|
| printing temp. | DF | 225±10˚C |
Packaging
PLA Satin is available in nearly any type of packaging and labelling. Ask our team to help you customizing your product.Additional information
Due to its low tendency to warp PLA SATIN can also be printed without a heated bed. If you have a heated bed the recommended temperature is ± 50-60˚C. PLA SATIN can be used on all common desktop FDM or FFF technology 3D printers.
Please note: the parameters you use for printing with Satin can change the Satin effect on printed parts. Looking into the parameters and fine-tune the profile for your printer will benefit the Satin effect of your printed part.