PLA is a tough, easy to use high-grade PLA type of filament, ideal for 3D printing. Slightly modified, the filament retains the typical features of PLA, but makes it tougher and less brittle. Due to a low shrinkage factor, PLA will not deform after cooling. Poly Lactic Acid is a biodegradable plastic made from renewable natural resources and one of the most popular materials for 3D printing.
PLA features:
- Tougher and less brittle compared to regular PLA
- Easy to print at low temperature
- Low warping
- Biodegradable
- Limited smell
| Size | ø Tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
| Description | Test method | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,24 g/cc |
| MFR 210°C/2,16 kg | ISO 1133 | 9,56 gr/10 min |
| Tensile strength at yield | ISO 527 | 66 MPa |
| Elongation strain at break | ISO 527 | 2,3% |
| Elongation strain at yield | ISO 527 | 2,3% |
| Tensile (E) modulus | ISO 527 | 3027 MPa |
| Impact strength - Charpy method 23˚C | ISO 179 | 3,4 kJ/m² |
| Moisture absorption | ISO 62 | 1968 ppm |
| Vicat softening temp. | ISO 306 | 60°C |
| Glass transition temp. | ISO 11357 | 57°C |
| Description | Test method | Typical value |
|---|---|---|
| printing temp. | Internal method | 205±10˚C |
| melting temp. | ISO 11357 | 115±35°C |
Packaging
Additional information
Due to its low tendency to warp PLA can also be printed without a heated bed. If you have a heated bed the recommended temperature is
± 95-140˚F | ± 35-60˚C.
PLA can be used on all common desktop FDM or FFF technology 3D printers.